Related Steels Products

• High Speed Steel D2 Steel D2 Technical Data Tool Steel

  D2 Tool Steel. D2 Tool Steel is a versatile high carbon, high chromium, air hardening tool steel that is characterized by a relatively high attainable hardness and numerous, large, chromium rich alloy carbides in the microstructure. These carbides provide good resistance to wear from sliding contact with other metals and abrasive materials.

• high hardness steel, high hardness steel Suppliers and

  offers 17,876 high hardness steel products. About 10% of these are Steel Sheets, 0% are Stainless Steel Sheets, and 0% are Steel Round Bars. A wide variety of high hardness steel options are available to you, such as technique, standard, and surface treatment.

• Steel grades The Tool Hub

  blanking dies for stainless steel or metal sheets with high hardness. DC53SKD11 ModifiedThrough Hardened50 52High toughness chromium cold work tool steel, high temperature tempering after the heat treatment can reach the high hardness of 62 HRC, especial good for much EDM wire cut works to reduce the breakage.

• Case carburized stainless steel alloy for high temperature

  Jun 13, 1995 · The resultant articles exhibit a high surface hardness of at least 62 HRC at room temperature and at least about 58 HRC at elevated temperatures, approaching 800° F. (427° C.), while possessing excellent fracture toughness in the core over this temperature range. The articles made from the alloy, likewise, exhibit excellent corrosion resistance.

• Crucible Selector CPM® 3V

  It offers impact resistance greater than A2, D2, Cru Wear, or CPM M4, approaching the levels provided by S7 and other shock resistant grades. CPM 3V is intended to be used at 58/60 HRC in applications where chronic breakage and chipping are encountered in other tool steels, but where the wear properties of a high alloy steel are required.

• SAE AISI 4140 Steel Properties, Material Heat Treatment

  SAE AISI 4140 Alloy Steel. SAE 4140 (AISI 4140 steel) is a Cr Mo series (Chrome molybdenum series) low alloy steel, this material has high strength and hardenability, good toughness, small deformation during quenching, high creep strength and long lasting strength at high temperature. 4140 Steel Uses

• Steel Information CASiberia

  1095 was developed as a simple tool steel that proved very effective for knife blades when heat treated appropriately. The high carbon content allows the steel to be quenched to a hardness of HRc66, but for knife blades the steel is usually drawn back (tempered) to 56 58 HRc, which provides an optimum combination of hardness and toughness. 1095 Steel Composition0.95C 0.4Mn

• Tungsten/Chromium Carbide Coatings Extreme Coatings

  The main difference between these coatings is their maximum service temperature limitation. Tungsten carbide has a max temperature rating of 730 F (400C) and chromium carbide 1300F ( 725C). Chromium carbide is indicated where significant corrosion is expected or where high

• S7, D2, A2Difference in tool steel properties Paulo

  It is the softest of the steel formulations compared in this article, achieving a typical working hardness range between 48 58 HRC. Its sweet spot hardness is 54 56 HRC and a yield strength of 235 ksi at a 500 degree Fahrenheit temper. At those levels it achieves a good balance of strength and ductility.

• Stamping Die Material Types And Characteristics_Low alloy

  Recommended heat treatment process for CH 1 steelQuenching temperature 900~920 °C, oil cooling, 190~200 °C tempering 1~3 hours, hardness 58~62 HRC. (5) 6CrNiSiMnMoV (Code GD) SteelHigh toughness low alloy steel, hardenability, air quenching deformation, high wear resistance. Its strength and toughness are significantly higher than those

• 440C Stainless Steel Penn Stainless

  Grade 440C stainless steel is a high carbon martensitic stainless steel. It has high strength, moderate corrosion resistance, and good hardness and wear resistance. Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness and wear resistance of all the stainless alloys.

• S7, D2, A2Difference in tool steel properties Paulo

  It is the softest of the steel formulations compared in this article, achieving a typical working hardness range between 48 58 HRC. Its sweet spot hardness is 54 56 HRC and a yield strength of 235 ksi at a 500 degree Fahrenheit temper. At those levels it achieves a good balance of strength and ductility.

• Stamping Die Material Types And Characteristics_Low alloy

  Recommended heat treatment process for CH 1 steelQuenching temperature 900~920 °C, oil cooling, 190~200 °C tempering 1~3 hours, hardness 58~62 HRC. (5) 6CrNiSiMnMoV (Code GD) SteelHigh toughness low alloy steel, hardenability, air quenching deformation, high wear resistance. Its strength and toughness are significantly higher than those

• 440C Stainless Steel Penn Stainless

  Grade 440C stainless steel is a high carbon martensitic stainless steel. It has high strength, moderate corrosion resistance, and good hardness and wear resistance. Grade 440C is capable of attaining, after heat treatment, the highest strength, hardness and wear resistance of all the stainless alloys.

• AISI 4330, 4330V, 4145, 4150 alloy steel

  AISI 4330V description. High strength steel used in applications involving shock loading or stress concentration, for example drilling jars in oil and gas sectors or air frames and fasteners in aerospace industry.. AISI 4330V is basically AISI 4330 steel with strength and hardenability improved by the addition of vanadium.The type of 4330 steel with a significant addition of nickel is

• Bal tec Common Ball Materials

  The balls are heat treated to a hardness of 62 HRC minimum. They are strongly attracted by a magnet. Hardened Stainless Steel Balls are widely used in bearings and valves, and are manufactured from steel AISI type 440C. Hardness is 58 HRC minimum. They are strongly attracted by a magnet. Unhardened Stainless Steel Balls

• Heat Treatment Haynes International

  The heat treatment of the HAYNES® and HASTELLOY® alloys is a very important topic. In the production of these wrought materials, there are many hot and cold reduction steps, between which intermediate heat treatments are necessary, to restore the optimum properties, in particular ductility.

• A2 1.2363 SKD12 Tool Steel Heat Treatment Songshun

  The machinability is also better than SKD11 steel. Using 1.2363 steel can increase the service life of the mold and get higher production efficiency. High quench hardening ability. so it can efficiently avoid the defects which be caused by insufficient hardness during vacuum heat treatment.